Elastic modulus (EM), initial fracture strength (FS) and flexural fatigue limit (FFL) of dental restorative materials were measured in a simulated oral environment to correlate mechanical response under the influence of water with the chemical nature of the test materials under investigation. One resin composite (RC; Tetric Ceram, Ivoclar-Vivadent Corp., Liechtenstein), an ion-leaching resin composite (ILRC; Ariston pHc, Ivoclar-Vivadent Corp., Liechtenstein) a compomer (CO; Dyract AP, Dentsply Corp., USA) and a glass-ionomer cement (GIC; Ketac Molar, 3MEspe Corp., Germany) were tested. Static EM, FS and dynamic FFL experiments were performed. The FFL was determined under cyclic loading for 10(5) cycles in terms of a staircase approach. The materials were stored for 1, 8, 30, 90 and 180 days in 37 degrees C distilled water, respectively. The RC degraded over time due to water adsorption followed by failure within the resin matrix. The ILRC suffered from a pronounced decrease in FS as well as in FFL due to a constant ion-leaching and macroscopic crack growth. CO failed over time due to resin-filler interface cracking. The GIC exhibited improved mechanical performance over time due to a post-hardening mechanism. The results reveal the necessity for substantial preclinical evaluation of direct restorative materials. The material parameters under investigation are capable of predicting clinical performance over time.
|
| pubmed:language |
eng
|
| pubmed:journal | |
| pubmed:status |
PubMed-not-MEDLINE
|
| pubmed:month |
Dec
|
| pubmed:issn |
0957-4530
|
| pubmed:author | |
| pubmed:issnType |
Print
|
| pubmed:volume |
14
|
| pubmed:owner |
NLM
|
| pubmed:authorsComplete |
Y
|
| pubmed:pagination |
1047-53
|
| pubmed:year |
2003
|
| pubmed:articleTitle |
Time-dependent strength and fatigue resistance of dental direct restorative materials.
|