rdf:type |
|
|
lifeskim:mentions |
|
|
pubmed:issue |
12
|
|
pubmed:dateCreated |
1992-6-15
|
|
pubmed:abstractText |
A 4-META-containing adhesive was evaluated for its ability to bond a composite resin and two types of amalgam to dentin. One group of composite resin was tested after 24 hours and another group after 24 hours of thermocycling. Shear bond strengths were: composite resin at 24 hours = 22.38 MPa; thermocycled composite resin = 20.86 MPa; spherical alloy = 3.38 MPa; admixed alloy = 3.84 MPa. Microleakage was evaluated after the 4-META adhesive was applied to cavity preparations and compared to that of a group treated with a cavity varnish. There was statistically significantly less microleakage in the 4-META group at both the occlusal and gingival margins.
|
|
pubmed:language |
eng
|
|
pubmed:journal |
|
|
pubmed:citationSubset |
D
|
|
pubmed:chemical |
http://linkedlifedata.com/resource/pubmed/chemical/4-methacryloxyethyltrimellitic...,
http://linkedlifedata.com/resource/pubmed/chemical/Amalgambond,
http://linkedlifedata.com/resource/pubmed/chemical/Cavi-Line,
http://linkedlifedata.com/resource/pubmed/chemical/Coloring Agents,
http://linkedlifedata.com/resource/pubmed/chemical/Composite Resins,
http://linkedlifedata.com/resource/pubmed/chemical/Dental Alloys,
http://linkedlifedata.com/resource/pubmed/chemical/Dental Amalgam,
http://linkedlifedata.com/resource/pubmed/chemical/Dental Materials,
http://linkedlifedata.com/resource/pubmed/chemical/Dispersalloy,
http://linkedlifedata.com/resource/pubmed/chemical/Methacrylates,
http://linkedlifedata.com/resource/pubmed/chemical/Organic Chemicals,
http://linkedlifedata.com/resource/pubmed/chemical/Valiant PhD
|
|
pubmed:status |
MEDLINE
|
|
pubmed:month |
Dec
|
|
pubmed:issn |
0033-6572
|
|
pubmed:author |
|
|
pubmed:issnType |
Print
|
|
pubmed:volume |
22
|
|
pubmed:owner |
NLM
|
|
pubmed:authorsComplete |
Y
|
|
pubmed:pagination |
979-83
|
|
pubmed:dateRevised |
2006-11-15
|
|
pubmed:meshHeading |
pubmed-meshheading:1813915-Coloring Agents,
pubmed-meshheading:1813915-Composite Resins,
pubmed-meshheading:1813915-Dental Alloys,
pubmed-meshheading:1813915-Dental Amalgam,
pubmed-meshheading:1813915-Dental Bonding,
pubmed-meshheading:1813915-Dental Cavity Lining,
pubmed-meshheading:1813915-Dental Leakage,
pubmed-meshheading:1813915-Dental Materials,
pubmed-meshheading:1813915-Dental Stress Analysis,
pubmed-meshheading:1813915-Dentin,
pubmed-meshheading:1813915-Humans,
pubmed-meshheading:1813915-Materials Testing,
pubmed-meshheading:1813915-Methacrylates,
pubmed-meshheading:1813915-Organic Chemicals,
pubmed-meshheading:1813915-Tensile Strength
|
|
pubmed:year |
1991
|
|
pubmed:articleTitle |
Dentinal bond strengths and microleakage of a 4-META adhesive to amalgam and composite resin.
|
|
pubmed:affiliation |
Department of General Practice, University of Texas, Health Science Center at San Antonio 78284-7914.
|
|
pubmed:publicationType |
Journal Article,
Comparative Study
|