Rubber dam clamps fracture infrequently during use. There are no American National Standards Institute or International Standards Organization standards for their manufacture. The purpose of this study was to measure the hardness of the clamps and test their resistance to a stress-corrosion test. Upper molar, lower molar, and premolar clamps were obtained from two manufacturers (A, B). The Rockwell C hardness at four sites on the bow of each clamp was then determined. Fresh clamps were placed on blocks corresponding to the average buccal-lingual dimension of the tooth on which they would be used. These blocks were then submerged in room temperature 5.25% sodium hypochlorite for 20 min and then allowed to air dry for 30 min. This was repeated 10 times. Rockwell C hardness values ranged from C30 to 38, with the clamps of manufacturer B being significantly harder. None of the clamps from manufacturer B cracked or corroded. When a third batch received from manufacturer A was tested in the same manner, none of the clamps fractured or corroded either.
|
| pubmed:language |
eng
|
| pubmed:journal | |
| pubmed:citationSubset |
D
|
| pubmed:chemical | |
| pubmed:status |
MEDLINE
|
| pubmed:month |
Jun
|
| pubmed:issn |
0099-2399
|
| pubmed:author | |
| pubmed:issnType |
Print
|
| pubmed:volume |
23
|
| pubmed:owner |
NLM
|
| pubmed:authorsComplete |
Y
|
| pubmed:pagination |
397-8
|
| pubmed:dateRevised |
2006-11-15
|
| pubmed:meshHeading | |
| pubmed:year |
1997
|
| pubmed:articleTitle |
Hardness and stress-corrosion of rubber dam clamps.
|
| pubmed:affiliation |
Department of Stomatology, University of Texas-Houston Health Science Center 77030-3402, USA.
|
| pubmed:publicationType |
Journal Article,
Comparative Study
|