pubmed:abstractText
A new adhesive fissure sealant, which consists of a solution of 3% 2-hydroxy-3-beta-naphthoxypropyl methacrylate in methyl methacrylate (MMA), poly-MMA powder and an oxidized tri-n-butyl borane, a polymerization initiator, was developed. Tensile bond strength between an acid-etched bovine enamel and a poly-MMA bar joined by this sealant was 60 kg/cm2, and the value did not decrease much after 30 days immersion in water at 37 degrees C. Penetration of fuchsin into the sealant-enamel interface during a percolation test was not observed. SEM observation showed no voids between the enamel and the cured sealant.
pubmed:language
eng
pubmed:journal
pubmed:citationSubset
IM
pubmed:chemical
pubmed:status
MEDLINE
pubmed:month
Mar
pubmed:issn
0021-9304
pubmed:author
pubmed:issnType
Print
pubmed:volume
12
pubmed:owner
NLM
pubmed:authorsComplete
Y
pubmed:pagination
149-65
pubmed:dateRevised
2008-11-21
pubmed:meshHeading
pubmed:year
1978
pubmed:articleTitle
Development of adhesive pit and fissure sealants using a MMA resin initiated by a tri-n-butyl borane derivative.
pubmed:publicationType
Journal Article