The aim of this study was to investigate the bond durability of heat-polymerized denture base resin to cast CP Ti and Co-Cr alloy. The alloy specimens were divided into five groups: 1) airborne-particle abraded with 50 µm alumina (SAND), 2) Rocatec tribochemical silica coating system (RO), 3) air-abraded followed by application of Epricord Opaque Primer (EP), 4) air-abraded followed by application of Super Bond C&B liquid (SB), 5) air-abraded followed by application of Alloy Primer (AL). Heat-polymerized denture resin was applied to the bonding area and polymerized according to the manufacturer's instructions. The halves of all specimens were thermocycled up to 10,000 cycles. Before thermocycling SB and AL showed significantly higher shear bond strengths than SAND, RO, EP for both metals. The shear bond strength of AL group after thermocycling was significantly higher than that of the other groups.
|
|
pubmed:language |
eng
|
|
pubmed:journal |
|
|
pubmed:citationSubset |
D
|
|
pubmed:chemical |
http://linkedlifedata.com/resource/pubmed/chemical/Acrylic Resins,
http://linkedlifedata.com/resource/pubmed/chemical/Alloy Primer,
http://linkedlifedata.com/resource/pubmed/chemical/Aluminum Oxide,
http://linkedlifedata.com/resource/pubmed/chemical/Boron Compounds,
http://linkedlifedata.com/resource/pubmed/chemical/Carbon Compounds, Inorganic,
http://linkedlifedata.com/resource/pubmed/chemical/Chromium Alloys,
http://linkedlifedata.com/resource/pubmed/chemical/Composite Resins,
http://linkedlifedata.com/resource/pubmed/chemical/Dental Cements,
http://linkedlifedata.com/resource/pubmed/chemical/Dental Materials,
http://linkedlifedata.com/resource/pubmed/chemical/Lucitone,
http://linkedlifedata.com/resource/pubmed/chemical/Methacrylates,
http://linkedlifedata.com/resource/pubmed/chemical/Methylmethacrylates,
http://linkedlifedata.com/resource/pubmed/chemical/Resin Cements,
http://linkedlifedata.com/resource/pubmed/chemical/Rocatec,
http://linkedlifedata.com/resource/pubmed/chemical/Silicon Compounds,
http://linkedlifedata.com/resource/pubmed/chemical/Silicon Dioxide,
http://linkedlifedata.com/resource/pubmed/chemical/Super-bond,
http://linkedlifedata.com/resource/pubmed/chemical/Thiones,
http://linkedlifedata.com/resource/pubmed/chemical/Titanium,
http://linkedlifedata.com/resource/pubmed/chemical/epricord,
http://linkedlifedata.com/resource/pubmed/chemical/silicon carbide
|
|
pubmed:status |
MEDLINE
|
|
pubmed:issn |
1881-1361
|
|
pubmed:author |
|
|
pubmed:issnType |
Electronic
|
|
pubmed:volume |
30
|
|
pubmed:owner |
NLM
|
|
pubmed:authorsComplete |
Y
|
|
pubmed:pagination |
143-50
|
|
pubmed:meshHeading |
pubmed-meshheading:21383520-Acrylic Resins,
pubmed-meshheading:21383520-Aluminum Oxide,
pubmed-meshheading:21383520-Boron Compounds,
pubmed-meshheading:21383520-Carbon Compounds, Inorganic,
pubmed-meshheading:21383520-Chromium Alloys,
pubmed-meshheading:21383520-Composite Resins,
pubmed-meshheading:21383520-Dental Bonding,
pubmed-meshheading:21383520-Dental Cements,
pubmed-meshheading:21383520-Dental Etching,
pubmed-meshheading:21383520-Dental Materials,
pubmed-meshheading:21383520-Dental Polishing,
pubmed-meshheading:21383520-Dental Stress Analysis,
pubmed-meshheading:21383520-Denture Bases,
pubmed-meshheading:21383520-Hot Temperature,
pubmed-meshheading:21383520-Humans,
pubmed-meshheading:21383520-Materials Testing,
pubmed-meshheading:21383520-Methacrylates,
pubmed-meshheading:21383520-Methylmethacrylates,
pubmed-meshheading:21383520-Microscopy, Electron, Scanning,
pubmed-meshheading:21383520-Polymerization,
pubmed-meshheading:21383520-Resin Cements,
pubmed-meshheading:21383520-Shear Strength,
pubmed-meshheading:21383520-Silicon Compounds,
pubmed-meshheading:21383520-Silicon Dioxide,
pubmed-meshheading:21383520-Stress, Mechanical,
pubmed-meshheading:21383520-Surface Properties,
pubmed-meshheading:21383520-Thiones,
pubmed-meshheading:21383520-Titanium
|
|
pubmed:year |
2011
|
|
pubmed:articleTitle |
Effect of surface preparation on the bond strength of heat-polymerized denture base resin to commercially pure titanium and cobalt-chromium alloy.
|
|
pubmed:affiliation |
Division of Removable Prosthodontics, Department of Oral Rehabilitation, Fukuoka Dental College, 2-15-1 Tamura, Sawara-Ku, Fukuoka 814-0193, Japan. tomokawa@college.fdcnet.ac.jp
|
|
pubmed:publicationType |
Journal Article,
Comparative Study,
Randomized Controlled Trial
|