The tensile strength and depth of weld of two cobalt chromium alloys before and after laser welding with and without an argon gas atmosphere were investigated. Using two cobalt chromium alloys, rod shaped specimens (5 cm x 1.5 mm) were cast. Specimens were sand blasted, sectioned and welded with a pulsed Nd: YAG laser welding machine and tested in tension using an Instron universal testing machine. A statistically significant difference in tensile strength was observed between the two alloys. The tensile strength of specimens following laser welding was significantly less than the unwelded controls. Scanning electron microscopy showed that the micro-structure of the cast alloy was altered in the region of the weld. No statistically significant difference was found between specimens welded with or without an argon atmosphere.
pubmed:language
eng
pubmed:journal
pubmed:citationSubset
D
pubmed:chemical
pubmed:status
MEDLINE
pubmed:month
Jun
pubmed:issn
0965-7452
pubmed:author
pubmed:issnType
Print
pubmed:volume
18
pubmed:owner
NLM
pubmed:authorsComplete
Y
pubmed:pagination
60-5
pubmed:meshHeading
pubmed:year
2010
pubmed:articleTitle
Tensile strength of laser welded cobalt-chromium alloy with and without an argon atmosphere.
pubmed:publicationType
Journal Article