pubmed:abstractText
The preparation of hydroxyapatite (HA) coatings via a versatile right-angle magnetron sputtering (RAMS) approach for use as a biomaterial has recently been reported. RAMS coatings show some advantages over conventionally sputtered films in that room temperature deposition yields nanocrystalline and nearly stoichiometric HA coatings under appropriate conditions, thereby avoiding the troublesome post deposition annealing treatment. In this article, we present an exploratory study of the biocompatibility of RAMS HA coatings deposited on metallic substrates. RAMS HA coatings with a thickness around 500nm were prepared on various substrates. X-ray diffraction (XRD) analysis showed that the as-deposited HA coatings were polycrystalline with some strongly preferred orientations. Atomic force microscopy (AFM) results showed that the coatings were rather smooth with surface roughness on the order of 10 nm. X-ray photoelectron spectroscopy (XPS) confirmed that the surface chemistry was nearly stoichiometric. To study the biocompatibility of these coatings, murine pre-osteoblastic MC3T3-E1 cells were seeded onto various substrates. Cell density counts using fluorescence microscopy showed that the best osteoblast proliferation is achieved on an HA RAMS-coated titanium substrate. Additionally, in preliminary studies the influence of Zn, Mg, and Al incorporation in the HA crystal lattice on the in vitro behavior was also evaluated. These experiments demonstrate that RAMS is a promising coating technique for biomedical applications.
pubmed:language
eng
pubmed:journal
pubmed:citationSubset
IM
pubmed:chemical
pubmed:status
MEDLINE
pubmed:month
Jun
pubmed:issn
1552-4965
pubmed:author
pubmed:issnType
Electronic
pubmed:day
1
pubmed:volume
93
pubmed:owner
NLM
pubmed:authorsComplete
Y
pubmed:pagination
878-85
pubmed:meshHeading
pubmed:year
2010
pubmed:articleTitle
Osteoblast proliferation on hydroxyapatite coated substrates prepared by right angle magnetron sputtering.
pubmed:affiliation
Department of Physics and Astronomy, Northwestern University, Evanston, Illinois 60208, USA. z.hong.nu@gmail.com
pubmed:publicationType
Journal Article, Research Support, U.S. Gov't, Non-P.H.S.