The fabrication process, compressive strength and biocompatibility of porous beta-tricalcium phosphate (beta-TCP) ceramic scaffolds reinforced with 45P(2)O(5)-22CaO-25Na(2)O-8MgO bioglass (beta-TCP/BG) were investigated for their suitability as bone engineering materials. Porous beta-TCP/BG scaffolds with macropore sizes of 200-500 muicrom were prepared by coating porous polyurethane template with beta-TCP/BG slurry. The beta-TCP/BG scaffolds showed interconnected porous structures and exhibited enhanced mechanical properties to those pure beta-TCP scaffolds. In order to assess the effects of chemical composition of this bioglass on the behavior of osteoblasts cultured in vitro, porous scaffolds were immersed in simulated body fluid (SBF) for 2 weeks, and original specimens (without soaked in SBF) seeded with MC3T3-E1 were cultured for the same period. The ability of inducing apatite crystals in simulated body fluid and the attachment of osteoblasts were examined. Results suggest that apatite agglomerates are formed on the surface of the beta-TCP/BG scaffolds and its Ca/P molar ratio is approximately 1.42. Controlling the crystallization from the beta-TCP/BG matrix could influence the releasing speed of inorganic ions and further adjust the microenvironment of the solution around the beta-TCP/BG, which could improve the interaction between osteoblasts and the scaffolds.
pubmed:language
eng
pubmed:journal
pubmed:citationSubset
IM
pubmed:chemical
pubmed:status
MEDLINE
pubmed:month
Jan
pubmed:issn
0957-4530
pubmed:author
pubmed:issnType
Print
pubmed:volume
20
pubmed:owner
NLM
pubmed:authorsComplete
Y
pubmed:pagination
351-8
pubmed:meshHeading
pubmed:year
2009
pubmed:articleTitle
Fabrication and biological characteristics of beta-tricalcium phosphate porous ceramic scaffolds reinforced with calcium phosphate glass.
pubmed:affiliation
Tianjin University, Tianjin, 300072, People's Republic of China.
pubmed:publicationType
Journal Article, In Vitro, Research Support, Non-U.S. Gov't