pubmed:abstractText |
The present research describes synthesis of highly sinterable, nano-sized hydroxyapatite (HAp) powders using a wet chemical route with recycled eggshell and phosphoric acid as calcium and phosphorous sources. The raw eggshell was easily turned to CaO by the calcining process, and phosphoric acid was mixed with the calcined eggshell by the wet, ball-milling method. The crystalline development and microstructures of the synthesized powders and sintered samples were examined by X-ray diffractometry and scanning electron microscopy, respectively. The observed phases on the powder synthesis process were dependent on the mixing ratio (wt%) of the calcined eggshell to phosphoric acid and the heating temperature. The ball-milled, nano-sized HAp powder, which has an average particle size of 70 nm, was fully densified at 1300 degrees C for 1h. The Ca/P ratio for stoichiometric composition of HAp was controlled by adjustment of the mixing ratio.
|