The dynamic recrystallization as well as meta-dynamic and static recrystallization of the nickel-based alloy 80A was investigated by means of electron backscatter diffraction (EBSD). Specimens were hot compressed at a temperature of 1120 degrees C and a strain rate of 0.1/s at varying strain and soak times to describe the recrystallization behaviour. Various approaches were tested in order to differentiate between recrystallized and deformed grains based on EBSD data. The grain orientation spread was clearly found to be the most reliable procedure. A high twinning of the recrystallized grains was observed, and as a consequence the measured grain size was strongly dependent on whether the coherent and incoherent twin boundaries were regarded as genuine boundaries or removed.
pubmed:language
eng
pubmed:journal
pubmed:status
PubMed-not-MEDLINE
pubmed:month
Sep
pubmed:issn
0022-2720
pubmed:author
pubmed:issnType
Print
pubmed:volume
227
pubmed:owner
NLM
pubmed:authorsComplete
Y
pubmed:pagination
267-74
pubmed:year
2007
pubmed:articleTitle
Recrystallization behaviour of the nickel-based alloy 80 A during hot forming.
pubmed:affiliation
Research Institute for Electron Microscopy, Graz University of Technology, Steyrergasse 17, A-8010 Graz, Austria. stefan.mitsche@felmi-zfe.at
pubmed:publicationType
Journal Article