A commercial software package, MAGMASOFT (MAGMA Giessereitechnologie GmbH, Aachen, Germany), was used to study shrinkage and gas porosity in titanium dental castings. A geometrical model for two simplified tooth crowns connected by a connector bar was created. Both mold filling and solidification of this casting model were numerically simulated. Shrinkage porosity was quantitatively predicted by means of a built-in feeding criterion. The risk of gas pore formation was investigated using the numerical filling and solidification results. The results of the numerical simulations were compared with experiments, which were carried out on a centrifugal casting machine with an investment block mold. The block mold was made of SiO2 based slurry with a 1 mm thick Zr2 face coat to reduce metal-mold reactions. Both melting and casting were carried out under protective argon (40 kPa). The finished castings were sectioned and the shrinkage porosity determined. The experimentally determined shrinkage porosity coincided with the predicted numerical simulation results. No apparent gas porosity was found in these model castings. Several running and gating systems for the above model casting were numerically simulated. An optimized running and gating system design was then experimentally cast, which resulted in porosity-free castings.
|
| pubmed:language |
eng
|
| pubmed:journal | |
| pubmed:status |
PubMed-not-MEDLINE
|
| pubmed:month |
Sep
|
| pubmed:issn |
0957-4530
|
| pubmed:author | |
| pubmed:copyrightInfo |
Copyright 1999 Kluwer Academic Publishers
|
| pubmed:issnType |
Print
|
| pubmed:volume |
10
|
| pubmed:owner |
NLM
|
| pubmed:authorsComplete |
Y
|
| pubmed:pagination |
519-25
|
| pubmed:year |
1999
|
| pubmed:articleTitle |
Numerical study of porosity in titanium dental castings.
|
| pubmed:affiliation |
Foundry Institute, University of Technology Aachen, Intzestr. 5, D-52072 Aachen, Germany. menghuai@gi.rwth-aachen.de
|
| pubmed:publicationType |
Journal Article
|