Age-hardening characteristics and precipitation behavior of Ag-25%Pd-3%In-1%Zn-0.5%Ir alloy were investigated in detail by means of hardness testing, X-ray diffraction, electron microscopy and resistivity measurement. The solution treating could be accomplished at 980 degrees C and the aging in the temperature range from 950 to 850 degrees C occurred by continuous precipitation. The aging in the temperature range from 850 to 450 degrees C occurred first, forming GP-zones with a hardness increase and then in overaging stage by forming discontinuous precipitation, which consisted of lamellae of solute (Pd, In, Zn) depleted Ag-rich phase and (Pd,Ag)3(In,Zn) intermetallic phase. The hardness increased very fast to its peak in 10 min during aging at temperatures between 450 and 550 degrees C.
pubmed:language
eng
pubmed:journal
pubmed:status
PubMed-not-MEDLINE
pubmed:month
Jan
pubmed:issn
0957-4530
pubmed:author
pubmed:copyrightInfo
Copyright 2000 Kluwer Academic Publishers
pubmed:issnType
Print
pubmed:volume
11
pubmed:owner
NLM
pubmed:authorsComplete
Y
pubmed:pagination
43-8
pubmed:year
2000
pubmed:articleTitle
Precipitation behavior of Ag-Pd-In dental alloys.
pubmed:affiliation
Department of Materials Science and Engineering, Korea Advanced Institute of Science and Technology, 373-1 Kusung-Dong, Yusung-Gu, Taejon, 305-701, South Korea. s_syc@cais.kaist.ac.kr
pubmed:publicationType
Journal Article