A commercial glass-ionomer (Fuji II) was studied using different NMR techniques. 1H and 19F stray-field imaging (STRAFI) were used to monitor the curing kinetics of the cement and two processes were distinguished: the gelation and maturation phases. Characterization of the aluminium and silicon species present in the glass component and cement was performed by conventional 27Al and 29Si MAS and two-dimensional 27Al triple quantum MAS NMR (MQMAS) techniques. Quantification of the aluminium in the glass component and in the cement indicates the leaching of about 32% of the 4-coordinate aluminium, about 100% of the 5-coordinate aluminium and about 41% of the 6-coordinate aluminium, during the setting reaction. It is also shown that the 5-coordinate aluminium is only present in the surface layer created by the acid attack during the cement formation process. In the cement, silicon maintains species with four bridging oxygens after the leaching of tetrahedral (4-coordinate) aluminium. The silicon analysis correlates well with the aluminium determinations.
pubmed:language
eng
pubmed:journal
pubmed:citationSubset
IM
pubmed:chemical
pubmed:status
MEDLINE
pubmed:month
Mar
pubmed:issn
0957-4530
pubmed:author
pubmed:issnType
Print
pubmed:volume
15
pubmed:owner
NLM
pubmed:authorsComplete
Y
pubmed:pagination
201-8
pubmed:dateRevised
2006-11-15
pubmed:meshHeading
pubmed:year
2004
pubmed:articleTitle
Stray-field imaging and multinuclear magnetic resonance spectroscopy studies on the setting of a commercial glass-ionomer cement.
pubmed:affiliation
Departamento de Engenharia de Materiais, Instituto Superior Técnico, Universidade Técnica de Lisboa, Av Rovisco Pais, 1, 1049-001 Lisboa, Portugal.
pubmed:publicationType
Journal Article, In Vitro, Research Support, Non-U.S. Gov't