We have developed a titanium-aluminium alloy with the inert alloying element niobium. The optimal composition was found to be Ti-6Al-7Nb (Protasul-100). This custom-made alloy designed for implants shows the same alpha/beta structure as Ti-6Al-4V and exhibits equally good mechanical properties. The corrosion resistance of Ti-6Al-7Nb in sodium chloride solution is equivalent to that of pure titanium and Ti-6Al-4V. This is due to a very dense and stable passive layer. Highly stressed anchorage stems of different hip prosthesis designs have been made from hot-forged Ti-6Al-7Nb. The polished surfaces of hip, knee and wrist joints made of Ti-6Al-7Nb and articulating against polyethylene are surface-treated by means of a very hard and 3-5 microns thick titanium nitride coating (Tribosul-TiN) or by oxygen diffusion hardening (Tribosul-ODH) to a depth of 30 microns.
|
| pubmed:language |
eng
|
| pubmed:journal | |
| pubmed:citationSubset |
IM
|
| pubmed:chemical | |
| pubmed:status |
MEDLINE
|
| pubmed:issn |
0142-9612
|
| pubmed:author | |
| pubmed:issnType |
Print
|
| pubmed:volume |
13
|
| pubmed:owner |
NLM
|
| pubmed:authorsComplete |
Y
|
| pubmed:pagination |
781-8
|
| pubmed:dateRevised |
2004-11-17
|
| pubmed:meshHeading | |
| pubmed:year |
1992
|
| pubmed:articleTitle |
Joint replacement components made of hot-forged and surface-treated Ti-6Al-7Nb alloy.
|
| pubmed:affiliation |
Sulzer Medical Technology Ltd., R&D Biomaterials, Winterthur, Switzerland.
|
| pubmed:publicationType |
Journal Article
|