Atomic force microscopy was used to study the growth modes (on SiO2, MoS2, and Au substrates) and the current-voltage (I-V) characteristics of organic semiconductor pentacene. Pentacene films grow on SiO2 substrate in a layer-by-layer manner with full coverage at an average thickness of 20 A and have the highest degree of molecular ordering with large dendritic grains among the pentacene films deposited on the three different substrates. Films grown on MoS2 substrate reveal two different growth modes, snowflake-like growth and granular growth, both of which seem to compete with each other. On the other hand, films deposited on Au substrate show granular structure for thinner coverages (no crystal structure) and dendritic growth for higher coverages (crystal structure). I-V measurements were performed with a platinum tip on a pentacene film deposited on a Au substrate. The I-V curves on pentacene film reveal symmetric tunneling type character. The field dependence of the current indicates that the main transport mechanism at high field intensities is hopping (Poole-Frenkel effect). From these measurements, we have estimated a field lowering coefficient of 9.77 x 10(-6) V-1/2 m1/2 and an ideality factor of 18 for pentacene.
pubmed:language
eng
pubmed:journal
pubmed:citationSubset
IM
pubmed:chemical
pubmed:status
MEDLINE
pubmed:month
Sep
pubmed:issn
1533-4880
pubmed:author
pubmed:issnType
Print
pubmed:volume
1
pubmed:owner
NLM
pubmed:authorsComplete
Y
pubmed:pagination
317-21
pubmed:dateRevised
2006-11-15
pubmed:meshHeading
pubmed:year
2001
pubmed:articleTitle
Morphology and current-voltage characteristics of nanostructured pentacene thin films probed by atomic force microscopy.
pubmed:affiliation
Department of Physics and Astronomy, University of Rochester, Rochester, New York 14627, USA.
pubmed:publicationType
Journal Article, Comparative Study, Research Support, U.S. Gov't, Non-P.H.S., Research Support, Non-U.S. Gov't, Evaluation Studies