Photocatalysts Pt/TiO2 coated on hollow glass beads were prepared by tetrabutyl titanate hydrolysis with Sodium silicate on hollow glass beads at various condition and loaded with platinum varying from 0.2% to 2.4% by weight. Sodium pentachlorophenolate (PCP-Na) solution were used to examined for their photoactivity and characterized by X-ray and BET. The results indicated that the optimization condition to prepare photocatalysts: Water to titanium alkoxides was 100, Sintering temperature was 650 degrees C, Diameter of hollow glass beads was 0.5 mm, TiO2: sodium silicate: hollow glass beads was 10:2.5:20, Platinum content of photocatalysts was about 1.4%-1.6%. When the experiments were carried out in such conditions, the initial concentration of PCP-Na was 100 mg/L, initial pH was 6.5, oxygen flux was 1.6 mL/s, illumination intensity was 30 kW.m-2, catalysts was 2 g/L, illumination time was 2 hours, respectively. Then the rates removals of PCP-Na could reach 92.0%.
|
pubmed:language |
chi
|
pubmed:journal | |
pubmed:citationSubset |
IM
|
pubmed:chemical |
http://linkedlifedata.com/resource/pubmed/chemical/Butanols,
http://linkedlifedata.com/resource/pubmed/chemical/Organometallic Compounds,
http://linkedlifedata.com/resource/pubmed/chemical/Pentachlorophenol,
http://linkedlifedata.com/resource/pubmed/chemical/Platinum,
http://linkedlifedata.com/resource/pubmed/chemical/Silicates,
http://linkedlifedata.com/resource/pubmed/chemical/Titanium,
http://linkedlifedata.com/resource/pubmed/chemical/sodium silicate,
http://linkedlifedata.com/resource/pubmed/chemical/tetrabutoxy titanium,
http://linkedlifedata.com/resource/pubmed/chemical/titanium dioxide
|
pubmed:status |
MEDLINE
|
pubmed:month |
Jan
|
pubmed:issn |
0250-3301
|
pubmed:author | |
pubmed:issnType |
Print
|
pubmed:day |
30
|
pubmed:volume |
23
|
pubmed:owner |
NLM
|
pubmed:authorsComplete |
Y
|
pubmed:pagination |
66-9
|
pubmed:dateRevised |
2006-11-15
|
pubmed:meshHeading |
pubmed-meshheading:11987410-Butanols,
pubmed-meshheading:11987410-Catalysis,
pubmed-meshheading:11987410-Hydrolysis,
pubmed-meshheading:11987410-Organometallic Compounds,
pubmed-meshheading:11987410-Pentachlorophenol,
pubmed-meshheading:11987410-Photochemistry,
pubmed-meshheading:11987410-Platinum,
pubmed-meshheading:11987410-Silicates,
pubmed-meshheading:11987410-Temperature,
pubmed-meshheading:11987410-Titanium
|
pubmed:year |
2002
|
pubmed:articleTitle |
[Tetrabutyl titanate hydrolysis prepared TiO2 photocatalysis loaded with platinum technology].
|
pubmed:affiliation |
Department of Environmental Engineering, Tsinghua University, Beijing 100084, China. xibeidou@263.net
|
pubmed:publicationType |
Journal Article,
English Abstract
|