| pubmed-article:14704046 | pubmed:abstractText | A new ternary ruthenium oxide Na(2)RuO(4) was prepared and shown to crystallize with a new structure type. Single crystal X-ray diffraction measurements reveal that Na(2)RuO(4) consists of RuO(4) chains made up of RuO(5) trigonal bipyramids by sharing axial corners. Na(2)RuO(4) is a magnetic semiconductor with a variable range hopping behavior, and its molar magnetic susceptibility chi(mol) has a broad maximum at approximately 74 K. The derivative d(chi(mol).T)/dT exhibits a peak at 37.7 K which has been confirmed by heat capacity measurement to be due to long-range antiferromagnetic ordering. | lld:pubmed |